Nickel 200 & Nickel 201: Nickel Alloys and Nickel Copper Alloys
Nickel 200 & Nickel 201: Nickel Alloys and Nickel Copper Alloys
Nickel 200 Alloy is a commercially pure nickel that exhibits good corrosion resistance and has rather low electrical resistivity. It’s used in caustic solutions, food handling equipment, and general corrosion-resistant parts and structures. Because it contains magnetic and mechanical properties, it can be used in devices that require magnetic actuated parts.
Nickel 201 Alloy is similar to Nickel 200 Alloy and is a low carbon modification of the 200 Alloy. It has a low annealed hardness and very low work-hardening rate. Those who use Nickel 201 Alloy find it desirable in deep drawing, spinning, and coining. It addition, it can be applied to corrosion-resistant equipment including but not limited to: caustic evaporators, spun anodes, and laboratory crucibles.
Nickel 205 Alloy contains controlled additions of magnesium and titanium (small amounts of both) and exhibits good oxidation resistance. It’s commonly used in support wires, vacuum tube components, pins, terminals, lead wires, and other electronic components of the like.
Nickel 270 Alloy is a high purity nickel alloy commonly used for electrical resistant thermometers.
Contact us for a quote on each of the Nickel Alloys described above.
CHEMICAL
COMPOSITION
|
TYPICAL
APPLICATIONS
|
Ni
- 99.0% min |
Food
Processing Equipment
|
C
- .15% max |
Electrical
& Electronic Parts
|
MN
- .35% max |
Aerospace
Components
|
S
- .010% max |
Rocket
Motor Casings
|
SI
- .35% max |
Transducers
|
CU
- .25% max |
|
FE
- .40% |
|
PHYSICAL PROPERTIES(ANNEALED
CONDITION)
Modulus
of Elasticity, Tension 10(******)psi - 29.6
Magnetic permeability at 200H(At 70 F) - 110-600
Electrical Resistivity, Microhm-cm(At 70 F)
- 9.5
Density,lb/cu.in. - .321
Coefficient of Thermal Expansion, in./in./ F
x 10(-******)
70 - 200 F ............................ 7.4
70 - 400 F ............................ 7.7
70 - 800 F ............................ 8.3
70 - 1000 F ........................... 8.5
|
NOMINAL
MECHANICAL PROPERTIES(ANNEALED CONDITION)
|
Ultimate Tensile Strength,psi
- 72,000
0.2% Offset Yield Strength,psi - 25,000
Elongation in 2 inches percent - 40
Density,lb/cu.in. - .321
Hardness, Rockwell - B61
|
THICKNESS |
.003" |
.020" |
.187" |
.500" |
.005" |
.030" |
.250" |
.750" |
.010 |
.040" |
.312" |
.812" |
.015" |
.062" |
.375 |
1.000" |
[TOP]
CHEMICAL
COMPOSITION
|
TYPICAL
APPLICATIONS
|
NI
- 99.0% min |
Heat
Exchanger Parts
|
C
- .02% max |
Electrical
Parts
|
MN
- .35% |
Aerospace
Components
|
S
- .010% max |
|
SI
- .35% max |
|
CU
- .25% max |
|
FE
- .40% |
|
PHYSICAL PROPERTIES(ANNEALED
CONDITION)
Modulus of Elasticity, Tension 10(******)psi
- 30
Magnetic permeability at 200H(At 70 F) - 110-600
Electrical Resistivity, Microhm-cm(At 70 F)
- 8.4
Density,lb/cu.in. - .321
Coefficient of Thermal Expansion, in./in./ F
x 10(-******)
70 - 200 F ............................ 7.3
70 - 400 F ............................ 7.7
70 - 800 F ............................ 8.4
70 - 1000 F ...........................
|
NOMINAL
MECHANICAL PROPERTIES(ANNEALED CONDITION)
|
Ultimate Tensile Strength,psi
- 59,000
0.2% Offset Yield Strength,psi - 15,000
Elongation in 2 inches percent - 40
Hardness, Rockwell - B55
|
THICKNESS |
.003" |
.020" |
.187" |
.500" |
.005" |
.030" |
.250" |
.750" |
.010 |
.040" |
.312" |
.812" |
.015" |
.062" |
.375 |
1.000" |
TK
|
Width
|
.003
|
SLIT
|
.004
|
TO
|
.005
|
YOUR
|
.010
|
WIDTH
|
.015
|
|
.020
|
|
.030
|
|
.040
|
|
.062
|
|
TK
|
Width
|
.003
|
12
|
.004
|
12
|
.005
|
12
|
.010
|
12
|
.015
|
12
|
.020
|
12
x 60
|
.050
|
.250
|
.375
|
.500
|
.750
|
1.0
|
1.5
|
Most
common diameters
|
Most
common sheet thicknesses nickel plate also available.
Nickels 205, 233 and 270 available on special
request. |