302 STAINLESS STEEL

NOMINAL DATA SHEET

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES (ANNEALED CONDITION)

CHROMIUM (Cr)	17-19	Ultimate Tensile Strength psi - 100,000
NICKEL (N)	8-10	0.2% Offset Yield Strength psi - 40,000
MAGANESE (Mn)	2.00 max	Percent Elongation in 2 inches - 50
CARBON (C)	0.15 max	Hardness Rockwell - B85
SULFUR (S)	0.030 max
PHOSPHORUS (P)	0.045 max
SILICON (Si)	1.00 max

PHYSICAL PROPERTIES(ANNEALED CONDITION) Modulus of Elasticity in tension psi: 28.0 x 10(6) Density(lbs./cu.in): 0.29 Electrical Resistivity at room temp.(microhm-cm): 72 Mean Coefficient of Thermal Expansion: in./in./ F(32-212 F) - 9.6 x 10(-6)

---

304 STAINLESS STEEL

NOMINAL DATA SHEET

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES (ANNEALED CONDITION)

Cr - 18-20	Ultimate Tensile Strength psi - 95,000
Ni - 8-10.50	0.2% Offset Yield Strength psi - 40,000
Mn - 2.00 max	Percent Elongation in 2 inches - 50
C - 0.08 max	Hardness Rockwell - B80
S - 0.030max
Si - 1.00 max
P - 0.045 max

PHYSICAL PROPERTIES(ANNEALED CONDITION) Modulus of Elasticity in tension psi - 28.0 x 10(******) Density(lbs./cu.in) - 0.29 Electrical Resistivity at room temp.(microhm-cm) - 72 Mean Coefficient of Thermal Expansion in./in./ F(32-212 F) - 9.6 x 10(-******) (******) = to the 6 (-******) = to the minus 6

---

304L STAINLESS STEEL

NOMINAL DATA SHEET

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES (ANNEALED CONDITION)

Cr - 18-20	Ultimate Tensile Strength psi - 90,000
Ni - 8-12	0.2% Offset Yield Strength psi - 40,000
Mn - 2.00 max	Percent Elongation in 2 inches - 50
C - 0.03 max	Hardness Rockwell - B80
S - 0.030max
Si - 1.00 max
P - 0.045 max

PHYSICAL PROPERTIES(ANNEALED CONDITION) Modulus of Elasticity in tension psi - 28.0 x 10(******) Density(lbs./cu.in) - 0.29 Electrical Resistivity at room temp.(microhm-cm) - 72 Mean Coefficient of Thermal Expansion in./in./ F(32-212 F) - 9.6 x 10(-******) (******) = to the 6 (-******) = to the minus 6

---

316 STAINLESS STEEL

NOMINAL DATA SHEET

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES (ANNEALED CONDITION)

Cr - 16-18	Ultimate Tensile Strength psi - 90,000
Ni - 10-14	0.2% Offset Yield Strength psi - 40,000
Mo - 2-3	Percent Elongation in 2 inches - 50
Mn - 2.00 max	Hardness Rockwell - B80
C - 0.03 max
Si - 1.00 max
S - 0.030max
P - 0.045 max

PHYSICAL PROPERTIES(ANNEALED CONDITION) Modulus of Elasticity in tension psi - 28.0 x 10(******) Density(lbs./cu.in) - 0.29 Electrical Resistivity at room temp.(microhm-cm) - 74 Mean Coefficient of Thermal Expansion in./in./ F(32-212 F) - 8.9 x 10(-******) (******) = to the 6 (-******) = to the minus 6

---

316L STAINLESS STEEL

NOMINAL DATA SHEET

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES (ANNEALED CONDITION)

Cr - 16-18	Ultimate Tensile Strength psi - 90,000
Ni - 10-14	0.2% Offset Yield Strength psi - 40,000
Mo - 2-3	Percent Elongation in 2 inches - 50
Mn - 2.00 max	Hardness Rockwell - B80
C - 0.03 max
Si - 1.00 max
S - 0.030max
P - 0.045 max

PHYSICAL PROPERTIES(ANNEALED CONDITION) Modulus of Elasticity in tension psi - 28.0 x 10(******) Density(lbs./cu.in) - 0.29 Electrical Resistivity at room temp.(microhm-cm) - 74 Mean Coefficient of Thermal Expansion in./in./ F(32-212 F) - 8.9 x 10(-******) (******) = to the 6 (-******) = to the minus 6

---

Available Sizes

SHEET	PLATE	COIL & FOIL	ROD
.050	.250	.001	.125
.062	.375	.002	.250
.078	.500	.003	.312
.109	.750	.004	.437
.125	1.00	.005	.500
.140		.010	.625
		.015	.750
		.020	.875
		.030	1.00
		.040	1.25
		.050	1.50
		.062	1.75
			2.00
			3.00
			4.00
			5.00
			6.00
			7.00
			8.00
			9.00
			10.0
			11.0
			12.0
			13.0
			14.0
			15.0
			16.0

*NOTE: Other sizes available upon request.

 

[TOP]