CDA
101
|
|
NOMINAL
DATA SHEET
|
| |
|
Typical
Nominal Chemistry
|
|
ASTM ALLOY NO.: B152
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x
27.68 = gms/cu cm at 20 C):.322
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20
C):226
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******)
from 68 F to 572 F
(20 C to 300 C):9.8
|
|
TENSILE
STRENGTH
|
YIELD
STRENGTH
(0.2% offset)
|
|
(x
1000 PSI (MPA = KSI x 6.8948)
|
|
annealed:
26 - 38
|
8
- 14
|
|
1/2
hard: 37 - 46
|
30
- 44
|
|
full
hard: 43 - 52
|
41
- 50
|
|
spring:
50 - 58
|
48
- 57
|
|
ELONGATION
% IN 2 inches (=% in 50mm)
|
|
annealed:
20 - 50
|
|
1/2
hard: 8 - 32
|
|
full
hard: 3 - 16
|
|
spring:
2 - 4
|
|
ROCKWELL
B HARDNESS
(.20 gauge and over (Rockwell F or 30 T where
noted)
|
|
annealed:
-
|
|
1/2
hard: 77 - 89 (F)
|
|
full
hard: 86 - 93(F)
|
|
spring:
91 - 97(F)
|
|
CDA
102
|
|
NOMINAL
DATA SHEET
|
| |
|
Typical
Nominal Chemistry
|
|
99.59%
CU min
|
|
.015-.040%
P
|
|
ASTM ALLOY NO.: B152
SAE ALLOY NO.: CA122
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x
27.68 = gms/cu cm at 20 C):.323
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20
C):196
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******)
from 68 F to 572 F
(20 C to 300 C):9.8
|
|
TENSILE
STRENGTH
|
YIELD
STRENGTH
(0.2% offset)
|
|
(x
1000 PSI (MPA = KSI x 6.8948)
|
|
annealed:
26 - 38
|
8
- 14
|
|
1/2
hard: 37 - 46
|
30
- 44
|
|
full
hard: 43 - 52
|
41
- 50
|
|
spring:
50 - 58
|
48
- 57
|
|
ELONGATION
% IN 2 inches (=% in 50mm)
|
|
annealed:
20 - 50
|
|
1/2
hard: 8 - 32
|
|
full
hard: 3 - 16
|
|
spring:
2 - 4
|
|
ROCKWELL
B HARDNESS
(.20 gauge and over (Rockwell F or 30 T where
noted)
|
|
annealed:
-
|
|
1/2
hard: 77 - 89 (F)
|
|
full
hard: 86 - 93(F)
|
|
spring:
91 - 97(F)
|
|
CDA
110
|
|
NOMINAL
DATA SHEET
|
| |
|
Typical
Nominal Chemistry
|
|
99.90%
CU min
|
|
.05
OXYGEN Max
|
|
ASTM ALLOY NO.: B152
SAE ALLOY NO.: CA110
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x
27.68 = gms/cu cm at 20 C):.322
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20
C):226
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******)
from 68 F to 572 F
(20 C to 300 C):9.8
|
|
TENSILE
STRENGTH
|
YIELD
STRENGTH
(0.2% offset)
|
|
(x
1000 PSI (MPA = KSI x 6.8948)
|
|
annealed:
26 - 38
|
8
- 14
|
|
1/2
hard: 37 - 46
|
30
- 44
|
|
full
hard: 43 - 52
|
41
- 50
|
|
spring:
50 - 58
|
48
- 57
|
|
ELONGATION
% IN 2 inches (=% in 50mm)
|
|
annealed:
20 - 50
|
|
1/2
hard: 8 - 32
|
|
full
hard: 3 - 16
|
|
spring:
2 - 4
|
|
ROCKWELL
B HARDNESS
(.20 gauge and over (Rockwell F or 30 T where
noted)
|
|
annealed:
-
|
|
1/2
hard: 77 - 89 (F)
|
|
full
hard: 86 - 93(F)
|
|
spring:
91 - 97(F)
|
|
CDA
101, CDA 102, ETP Copper 110
|
|
COPPER
ALLOYS 101/102/110
|
|
COIL
& FOIL
|
|
.003
.004
.005
.010
.015
.020
.032
.040
.050
.062
|
|
*NOTE: Other sizes available
upon request.
|
[TOP]
|
|
|
|